why choose us
'We understand your concern about costs and your requirements for quality.
cost-effective
Factory direct sales, reliable delivery. Urgent orders can be coordinated for priority production. Capable of collaborating with logistics companies to reduce transportation costs.
Mature technology,
Adopting a cotton canvas skeleton and a high wear-resistant rubber cover layer, the impact resistance is better than that of ordinary fabric belts, and the maintenance is simple.
Adapt to multiple scenarios
Has been verified on site for over 10 years in industries such as mining, ports, and building materials. Personalized customization to meet different production line layout needs.
Compliance certification
Has obtained multiple international certifications such as CE, ISO 9001, ISO 45001, ISO 14001, MA, etc
General Cotton Conveyor Belt factory
Main Technical Parameters
Type |
Textile type |
Strength per ply Min.(N/mm) |
Plies of fabric | Cover thickness(mm) | Belt width (mm) |
Cover grade | |
| Top cover | Bottom cover | ||||||
EP belt |
EP-100 | 100 | 2-8 |
2-16 |
0-10 |
300-3400 |
Abrasion resistant Impact resistant Heat resistant Oil resistant Acid/alkali resistant Fire resistant Etc. |
| EP-125 | 125 | ||||||
| EP-150 | 150 | ||||||
| EP-200 | 200 | ||||||
| EP-250 | 250 | ||||||
| EP-300 | 300 | ||||||
| EP-350 | 350 | ||||||
| EP-400 | 400 | ||||||
| EP-500 | 500 | ||||||
NN belt |
NN-100 | 100 | 2-10 |
||||
| NN-125 | 125 | ||||||
| NN-150 | 150 | ||||||
| NN-200 | 200 | ||||||
| NN-250 | 250 | ||||||
| NN-300 | 300 | ||||||
| NN-400 | 400 | ||||||
| NN-500 | 500 | ||||||
| CC belt | CC56 | 56 | 3-12 | ||||
Main technical indexes of GB / T 7984-2013
| Item | Type | ||||
| NN,EP,CC | |||||
| Adhesion strength | Between coating and belt cores | Thickness of coating layer>1.5mm ≥ N/mm |
3.5 | ||
| Thickness of coating layer 0.8~1.5mm More than N/mm |
3.2 | ||||
| Between layers ≥ N/mm | 4.5 | ||||
| Tensile strength value of full thickness belt / N / mm | 160 ~ 3150 | ||||
| Elongation of longitudinal reference force of full thickness belt / % ≤ | 4 | ||||
Coating performance |
H (sharp wear) |
D (high wear) |
L (moderate wear) |
||
| Breaking strength / MPa ≥ | 24 | 18 | 15 | ||
| Elongation at break / % ≥ | 450 | 400 | 350 | ||
| Abrasion / mm3 ≤ |
120 | 100 | 200 | ||
| Aging test(70ºC×168h) Median value of tensile strength and elongation |
It shall not be less than 75% of the corresponding value before aging. |
||||